Description
1. Nickel-cobalt-manganese terpolymer NCM523, single crystal structure, suitable for 4.35v high voltage applications, stable structure, high temperature storage performance, high gram capacity, high first efficiency, high compaction density, excellent cycle performance
2. Excellent processing performance, commercial mass production products, good quality, stable quality
3. Widely used in power tools, tablets, electronic toys, electric vehicles and energy storage and other products
4. It is convenient to carry out research on soft bag and power deduction
Physical property
PH~11.32
D10:2.24um
D50:4.20um
D90:7.56um
Gram volume:170mAh/g
Gram capacity power-off test conditions:25℃ 0.1C 3.0~4.3
D50:4.20umPH~11.32
D10:2.24um
D50:4.20um
Packaging, transportation, storage
1. Storage conditions: sealed at room temperature
2. Shelf life: 2 years from the production date
Product description, suggestions
TD:1.8g/cm³
BET:0.56m²/g
H₂O:289.6ppm
Free lithium:0.0249%
Element content:Li 7.60%,Co+Ni+Mn 58.95%,Ca 0.0055%,Cu 0.0001%,Fe 0.0018%,Mg 0.0028%,Na 0.0023%,Zn 0.0001%
1. Ternary materials with high maturity, polycrystalline ternary materials are relatively simple to use, and the compaction density is >3.4g/cc
2. For single crystal NCM523, due to the poor electronic conductivity of the material, it is necessary to optimize the pole-sheet formula